ViaPad® Release Films

ViaPad® Release Films

laminiermaschine-crop
 

UTF-100

UTF-100 is a high-temperature release film in thickness 25 µm made of modified PET with excellent separating properties and unique high temperature stability. Laminates pressed with UTF-100 can be further processed immediately without an additional after-treatment and remain solderable. UTF-100 release film contains no silicone and the press plates remain clean. UTF-100 is inexpensive and eco-friendly; no toxic fission products are produced during combustion. The film is also available in thickness 38 µm (UTF-150).

Delivery form: rolls with 1067 m and cuttings
Thickness: 25 µm (UTF-100); 38 µm (UTF-150)
Roll width: 305 – 1360 mm
Max. laminating temperature: about 210°C, depending on pressing conditions

Further information see technical datasheet:

Files:
UTF-100_TDS(3)
Date 05.07.2017 07:30:42 File Size 125.95 KB Download 1,330 Download

UTF-150_TDS(2)
Date 05.07.2017 07:31:30 File Size 125.86 KB Download 1,151 Download

 

VTF-400 RW

VTF-400 RW is a universal release film for pressing flexibel and rigid multilayers. The film has no surface coating. Nevertheless the product offers good release properties against many materials and resin systems. 

Delivery form: rolls and cuttings
Thickness: 40 µm
Roll width: 610 mm; 1285 mm (maximum)
Max. laminating temperature: 190 °C

 

TTF-25

TTF-25 release film is based on PTFE and therefore chemically inert and boasts a very high thermal stability. Making it particularly well-suited for laminating processes with very high pressing temperatures or application on surfaces that show contact reactions and react sensitively to polymer residues.

Delivery form: rolls and cuttings
Thickness: 25 µm; also available in further thicknesses (50 ... 500 µm).
Roll width: 460, 610, 660 mm
Max. laminating temperature: 260°C

Further information see technical datasheet:

TTF-25_TDS(1)
Date 05.07.2017 07:35:40 File Size 127.43 KB Download 1,030 Download

 

ATF-50

The release film ATF-50 is made of a special aluminium alloy and prevents the pressing-in of release film or pressure compensation material in the existing drill holes of the product to be pressed during lamination of coverlays on flexible and rigid-flexible PCBs. ATF-50 also prevents the "orange peel effect" on coverlays and is useful in suppressing image transfer. Positioning: between release film and press pad or pressure compensation foil.

Delivery form: rolls of 250 kg and cuttings (drilled or stamped on request)
Thickness: 50 µm
Roll width: 650 mm

Further information see technical datasheet:

ATF-50_TDS(1)
Date 05.07.2017 09:53:59 File Size 204.02 KB Download 996 Download

Contact Us

MSC Polymer AG
Am Boden 27
D-35460 Staufenberg-Mainzlar
Tel: +49 (0)6406-9149-0
Fax: +49 (0)6406-6782
Email: This email address is being protected from spambots. You need JavaScript enabled to view it.